316Ti stainless steel is based on 316 stainless steel by adding Ti to improve the resistance to intergranular corrosion. It is also a variant of 316 stainless steel and is used in equipment resistant to sulfuric acid, phosphoric acid, acetic acid, and acetic acid.

Physical properties:

316 stainless steel chemical composition

C:≤0.08

Si≤1.00

Mn≤2.00

P≤0.035

S≤0.030

Ni 11.00~14.00

Cr 16.00~19.00

Mo 1.80~2.50

Ti≥5*C%~0.70

Usually also called Mo2Ti or 316Ti

316L stainless steel (00Cr17Ni14Mo2) is an ultra-low carbon steel of 0Cr17Ni12Mo2, which is more resistant to intergranular corrosion than 0Cr17Ni12Mo2 (SUS316).

316L Stainless Steel Chemical Composition

C≤0.03

Si≤1.00 .

P≤0.035

S≤0.03

Ni: 12.0-15.0

Cr:16.0-18.0

Mo: 2.0-3.0

Tensile strength (Mpa) 620 MIN

Yield strength (Mpa) 310 MIN

Elongation (%) 30 MIN

Area reduction (%) 40 MIN

Features: Due to the addition of Mo, its corrosion resistance, atmospheric corrosion resistance and high temperature strength are particularly good, and it can be used under harsh conditions; excellent work hardening (non-magnetic); high temperature strength; Magnetic; cold-rolled products have good gloss and beautiful appearance; compared with 304L stainless steel, the price is higher.